Type T Boron Nitride Ceramics

It has stable chemical performance, does not react with molten metal at high temperature, improving alloy purity and good oxidation resistance, 400-500 degrees Celsius higher than graphite materials, and long service life.
  • T
  • FOTMA
  • Model: T
  • Density: >3.01g/cm³
  • Flexural Strength: >150Mpa
Quantity:
Type T Boron Nitride Ceramics
 
Product main performance parameters
The typical characteristics T
Chemical composition BN+TiB2+AlN
Density 3.01g/cm⊃3;
Modulus of elasticity 60-70Gpa
Flexural Strength 150Mpa
Coefficient of thermal expansion 4-610^-6/K)
Thermal conductivity at 20℃ 100/40W/mk
MAX-Temperature of use Oxidizing 900℃
Vacuum 1700℃
Inert 2000℃
RT Resistivity Ω.cm 300-2000

T.2

Product features and advantages:
  Unique craft formula, optimized composition structure, the material has excellent corrosion resistance, which greatly improves the service life.
  Using the international advanced vacuum hot pressing sintering method, the material has a fine structure, high density and superior physical properties.
  Stable chemical performance, does not react with molten metal at high temperature, improving alloy purity.
  Good oxidation resistance, 400-500 degrees Celsius higher than graphite materials, and long service life.
T.(二硼化钛陶瓷).1

Typical application:
  Conductive ceramic evaporation boat for vacuum aluminum plating
  Conductive ceramic crucible for high temperature electron beam evaporation
  Crucible and components for optical coating equipment
T.6
Previous: 
Next: 
We have an excellent technical team, our products in quality and quantity will make you satisfied, welcome to buy
  • +86-13995656368
  • Mon-Fri: 09:00AM - 06:00PM
  • Guanggu Avenue 52#, Hongshan, Wuhan, Hubei province, P.R.China. 430074
CONTACT US
Contact us NOW
Incorrect E-mail
Follow Us
Copyright ©2022 Hubei Fotma Machinery Co., Ltd.