Tungsten Carbide blades are well known for its sharp and durable. They can be used in a variety of industrial applications where extremely sharp cutting instruments are needed. Carbide blades are well suited to cutting reflective materials for plotting and sign making.
Although prone to chipping and breakage, when these pitfalls are avoided with the proper engineering,
tungsten carbide blades can sustain significant industrial stresses.
Tungsten carbide is less brittle than other metals, and thus can withstand the rigors of constant use easily. In fact, switching from blades made of other materials, such as titanium, carbon steel, and aluminum, to tungsten carbide blades may actually increase productivity. By handling tough jobs with ease, carbide blades can increase productivity by 10 or 20 percent in some industries. Some factories have found that although tungsten carbide material is often more expensive, its durability and ability to withstand pressure makes the extra cost worth it.
Grade List for Tungsten Carbide Blades
Grade | Density g/cm3 | Hardness HRA | Strength N/mm2 Min. | Applications | ISO grade |
YG6X | 14.8-15 | 91.7-93 | 1600 | High wear resistance and high strength; machining chilled cast iron and refractory steel, finishing of normal cast iron | K10(ANSI C-2) |
YT5 | 12.85-13.05 | 89.5-91 | 1700 | Excellent in strength, impact resistance and resistance to thermal shock; Rough turning, rough planning and semi planning of Carbon steel and alloy steel | P30(ANSI:C-5) |
YT15 | 11.2-11.4 | 92-93 | 1350 | Good wear resistance, with normal impact resistance; Semi finishing and finishing steel, cast steel, alloy steel. | P10 |
YT14 | 11.3-11.6 | 91.3-92.3 | 1450 | High in impact resistance and strength; Semi roughing and semi finishing of steel, cast steel and alloy steel. | P20-P30 |
YT535 | 12.6-12.8 | 90-91.5 | 1760 | High wear resistance and red hardness, high strength in use. For continuous rough turning and milling of cast or forged steel. | P30 |
ZP25 | 12.5-12.7 | 91.4-92.3 | 1750 | Fine in wear resistance and toughness; Rough turning, milling, planning and depth drilling of carbon steel, cast steel, manganese steel and alloy steel. | P20-P30 |
ZP35 | 12.6-12.8 | 90.5-91.5 | 1770 | A versatile grade, high in red hardness, strength and resistance to impact and thermal shocking. Roughing and strong cutting of steel and cast steel. | P30-P40 |
YG6 | 14.8-15 | 90-92 | 1650 | Good wear resistance, resistance to impact and thermal shocking. Semi finishing and finishing of cast iron, nonferrous metal, alloy and nonmetallic material. | K15-K20 |
YW1 | 13.25-13.5 | 92-93.2 | 1420 | A versatile grade, good in red hardness, able to endure normalimpact load; machining of refractory steel, high manganese steel, stainless steel, also suitable to the ormal steel and cast iron. | M10/P10 |
YW2 | 13.15-13.35 | 91.3-92.3 | 1600 | Good wear resistance and high strength, able to endure high impact load; Roughing, semi finishing of refractory steel, high manganese steel, stainless steel and high alloy steel, also suitable to the normal steel and cast iron. | M20/P20-30 |
YW2A | 12.85-13.05 | 91.5-92.5 | 1670 | Good red hardness, able to endure high impact load, is a all-purpose grade. Roughing, semi finishing of refractory steel, high manganese steel, stainless steel and high alloy steel, also suitable to cast iron. | M15/P15 |
ZM15 | 13.8-14.0 | 91-92.2 | 1720 | Good Red Hardness, high strength in use, capable of resisting high impact load. Finishing and semi-finishing of refractory steel, high manganese steel, and austenitic stainless steel, also suitable for Cast Iron. | M15 |
ZM30 | 13.5-13.7 | 90-91.5 | 1890 | High strength in use, capable of resisting high impact load. Roughing and semi-finishing of refractory steel, high manganese steel, stainless steel, etc. | M30 |
ZK10UF | 14.75-14.95 | 92.6-93.6 | 1690 | Fine-grained alloy, good wear resistance and high strength. Semi-finishing and finishing of cast iron and nonferrous metals. It is the unique material for making of solid carbide tools for holing. | K10-K15 |
ZK30UF | 14.3-14.55 | 91.2-92.2 | 2180 | Fine grain grade. Excellent wear resistance, high in strength and impact resistance. Machining of cast irons, nonferrous metals and non-metallic materials. It is the unique material of solid carbide tools for holing. | K30 |
Note: The specification dates just the standard, the actual specification for the products are much better than the standard. | |||||
Suggestion: We would like to recommend suitable grade depending on your machining materials. |
Surface Coating
Material | First layer | Second layer | Third layer | Fourth layer |
Ti8 | TiN | TiC | TiCN | TiN |
TAN | TiCN | TiC | Al2O3 | TiN |
Al2O3 | TiCN | TiC | Al2O3 | / |
Suggestion: We would like recommend suitable coated material depending on your requirement. |
Tungsten Carbide blades are well known for its sharp and durable. They can be used in a variety of industrial applications where extremely sharp cutting instruments are needed. Carbide blades are well suited to cutting reflective materials for plotting and sign making.
Although prone to chipping and breakage, when these pitfalls are avoided with the proper engineering,
tungsten carbide blades can sustain significant industrial stresses.
Tungsten carbide is less brittle than other metals, and thus can withstand the rigors of constant use easily. In fact, switching from blades made of other materials, such as titanium, carbon steel, and aluminum, to tungsten carbide blades may actually increase productivity. By handling tough jobs with ease, carbide blades can increase productivity by 10 or 20 percent in some industries. Some factories have found that although tungsten carbide material is often more expensive, its durability and ability to withstand pressure makes the extra cost worth it.
Grade List for Tungsten Carbide Blades
Grade | Density g/cm3 | Hardness HRA | Strength N/mm2 Min. | Applications | ISO grade |
YG6X | 14.8-15 | 91.7-93 | 1600 | High wear resistance and high strength; machining chilled cast iron and refractory steel, finishing of normal cast iron | K10(ANSI C-2) |
YT5 | 12.85-13.05 | 89.5-91 | 1700 | Excellent in strength, impact resistance and resistance to thermal shock; Rough turning, rough planning and semi planning of Carbon steel and alloy steel | P30(ANSI:C-5) |
YT15 | 11.2-11.4 | 92-93 | 1350 | Good wear resistance, with normal impact resistance; Semi finishing and finishing steel, cast steel, alloy steel. | P10 |
YT14 | 11.3-11.6 | 91.3-92.3 | 1450 | High in impact resistance and strength; Semi roughing and semi finishing of steel, cast steel and alloy steel. | P20-P30 |
YT535 | 12.6-12.8 | 90-91.5 | 1760 | High wear resistance and red hardness, high strength in use. For continuous rough turning and milling of cast or forged steel. | P30 |
ZP25 | 12.5-12.7 | 91.4-92.3 | 1750 | Fine in wear resistance and toughness; Rough turning, milling, planning and depth drilling of carbon steel, cast steel, manganese steel and alloy steel. | P20-P30 |
ZP35 | 12.6-12.8 | 90.5-91.5 | 1770 | A versatile grade, high in red hardness, strength and resistance to impact and thermal shocking. Roughing and strong cutting of steel and cast steel. | P30-P40 |
YG6 | 14.8-15 | 90-92 | 1650 | Good wear resistance, resistance to impact and thermal shocking. Semi finishing and finishing of cast iron, nonferrous metal, alloy and nonmetallic material. | K15-K20 |
YW1 | 13.25-13.5 | 92-93.2 | 1420 | A versatile grade, good in red hardness, able to endure normalimpact load; machining of refractory steel, high manganese steel, stainless steel, also suitable to the ormal steel and cast iron. | M10/P10 |
YW2 | 13.15-13.35 | 91.3-92.3 | 1600 | Good wear resistance and high strength, able to endure high impact load; Roughing, semi finishing of refractory steel, high manganese steel, stainless steel and high alloy steel, also suitable to the normal steel and cast iron. | M20/P20-30 |
YW2A | 12.85-13.05 | 91.5-92.5 | 1670 | Good red hardness, able to endure high impact load, is a all-purpose grade. Roughing, semi finishing of refractory steel, high manganese steel, stainless steel and high alloy steel, also suitable to cast iron. | M15/P15 |
ZM15 | 13.8-14.0 | 91-92.2 | 1720 | Good Red Hardness, high strength in use, capable of resisting high impact load. Finishing and semi-finishing of refractory steel, high manganese steel, and austenitic stainless steel, also suitable for Cast Iron. | M15 |
ZM30 | 13.5-13.7 | 90-91.5 | 1890 | High strength in use, capable of resisting high impact load. Roughing and semi-finishing of refractory steel, high manganese steel, stainless steel, etc. | M30 |
ZK10UF | 14.75-14.95 | 92.6-93.6 | 1690 | Fine-grained alloy, good wear resistance and high strength. Semi-finishing and finishing of cast iron and nonferrous metals. It is the unique material for making of solid carbide tools for holing. | K10-K15 |
ZK30UF | 14.3-14.55 | 91.2-92.2 | 2180 | Fine grain grade. Excellent wear resistance, high in strength and impact resistance. Machining of cast irons, nonferrous metals and non-metallic materials. It is the unique material of solid carbide tools for holing. | K30 |
Note: The specification dates just the standard, the actual specification for the products are much better than the standard. | |||||
Suggestion: We would like to recommend suitable grade depending on your machining materials. |
Surface Coating
Material | First layer | Second layer | Third layer | Fourth layer |
Ti8 | TiN | TiC | TiCN | TiN |
TAN | TiCN | TiC | Al2O3 | TiN |
Al2O3 | TiCN | TiC | Al2O3 | / |
Suggestion: We would like recommend suitable coated material depending on your requirement. |