Tantalum and Tantalum Alloy Products Processing
Sheet Thickness | Material | Processing Status. | Size | Stamping Performance |
General tolerance ±10% | Pure Ta≥99.95% | Cold rolled hard state | Cold rolled annealed state + pickling | Machining | maximum width | maximum length | Hardness (HV) | Flatness(%) | Punch strength cupping value(mm) | tensile strength(MPa) | Yield Strength(MPa) | elongation rate(%) |
0.10-0.15 | 0 | 0 | 0 | | 450 | 1000 | 115-135 | ≤5 | ≥ 12 | 207-481 | 138-414 | 15-20 |
0.16-0.19 | 0 | 0 | 0 | | 450 | 1000 | ≥ 12 |
0. 20-0. 29 | 0 | 0 | 0 | | 750 | 2000 | ≥ 12 |
0.30-0.39 | 0 | 0 | 0 | | 750 | 2000 | ≥ 12 |
0. 40-0. 49 | 0 | 0 | 0 | | 750 | 2000 | ≥ 15 |
0.50-0.59 | 0 | 0 | 0 | | 750 | 2000 | ≤4.5 | ≥ 15 |
0.60-0.69 | 0 | 0 | 0 | | 750 | 2000 | ≥ 15 |
0.70-0. 79 | 0 | 0 | 0 | 0 | 750 | 2000 | ≥ 15 |
0.80-0. 89 | 0 | 0 | 0 | 0 | 750 | 2000 | ≥ 15 |
0.90-0. 99 | 0 | 0 | 0 | 0 | 750 | 2000 | ≥ 15 |
1.0-1.4 | 0 | 0 | 0 | 0 | 750 | 2000 | ≥18 |
1.5-1.9 | 0 | 0 | 0 | 0 | 750 | 2000 | ≥18 |
2.0-2.4 | 0 | 0 | 0 | 0 | 700 | 2000 | ≥18 |
2.5-2.9 | 0 | 0 | 0 | 0 | 700 | 2000 | ≥18 |
3.0-3.4 | 0 | 0 | 0 | 0 | 700 | 2000 | ≥18 |
3.5-3.9 | 0 | 0 | 0 | 0 | 700 | 2000 | ≥20 |
4.0-4.9 | 0 | 0 | 0 | 0 | 700 | 2000 | ≥20 |
5.0-5.9 | 0 | 0 | 0 | 0 | 700 | 2000 | ≥20 |
6.0-6.9 | 0 | 0 | 0 | 0 | 700 | 2000 | ≥20 |
7.0-9.9 | 0 | 0 | 0 | 0 | 700 | 2000 | ≥20 |
10.0-11.9 | 0 | 0 | 0 | 0 | 700 | 2000 | ≥20 |
12.0-14.9 | 0 | 0 | 0 | 0 | 700 | 2000 | ≥20 |
15.0-19. 9 | 0 | 0 | 0 | 0 | 700 | 2000 | ≥20 |
20.0-25.0 | 0 | 0 | 0 | 0 | 700 | 2000 | ≥20 |