Tungsten wire
 
 
Application:
Type
Name
Kind
Applications
WAL1
Nonsag tungsten wires
L
Used in making single coiled filaments, filaments in fluorescent lamps and other components.
B
Used in making coiled coil and filaments in High power incandescent bulb, stage decoration lamp, heating filaments, halogen lamp, special lamps etc.
T
Used in making special lamps, exposition lamp of copy machine and lamps used in automobiles.
WAL2
Nonsag tungsten wires
J
Used in making filaments in incandescent bulb, fluorescent lamp, heating filaments, spring filaments, grid electrode, gas-discharge lamp, electrode and other electrode tubes parts.
Chemical Compositions:
Type
Kind
Tungsten content (%)
Total amount of impurity (%)
The content of each element (%)
Kalium content (ppm)
WAL1
L
99.95
0.05
0.01
50~80
B
60~90
T
70~90
 WAL2
J
40~50
Note: Kalium should not be taken as impurity, and tungsten powder must be have been washed by acid.

Specifications:
1.Tungsten Wires
Diameter (µm)
Wire Weight per 200mm in length (mg)
Wire Weight per 200mm in length for tolerance (%)
15 d18
> 0.3~0.98
Class A
Class B
+2.5
+3.0
18 < d 40
>0.98~4.85
+2.0
+2.5
40 < d 80
>4.85~19.39
+1.5
+2.0
80 < d 300
>19.39~30.30
+1.0
+1.5
300< d 400
>272.71~484.80
+0.5
+1.0
 
2.Cleaned Tungsten Wires
Diameter (µm)
Wire Weight per 200mm in length (mg)
Wire Weight per 200mm in length for tolerance (%)
Linearity
10 d 18
>0.3~0.98
Class A
Class B
Suspension length (%)
Chord high (mm)
+2.5
+3.0
-
-
18 < d 40
>0.98~4.85
+2.0
+2.5
-
-
40 < d 80
>4.85~19.39
+1.5
+2.0
90
-
80 < d100
>19.39~30.30
+1.0
+1.5
-
-
100< d 300
>30.30~272.71
+1.0
+1.5
-
8
300< d 400
>272.71~484.80
+0.5
+1.0
-
-
       
3.Tungsten Rods
Diameter (µm)
Diameter Tolerance
0.4 < d 1.0
Black Rods (%)
Ground Rods (mm)
+1.5
+0.02
1.0 < d 2.5
+2.0
+0.03
2.5 < d 5.8
+2.0
+0.05
5.8 < d 12.0
+2.0
+0.08
Direction for use
1. Aquadag layer on the surface of wire should be removed before using the wire is not suitable for contacting with iron, nickel, carbon, when the temperature is higher than 1000 . The wires should be preserved in dry room, in which the relative humidity should not surpass 65%, and keeping away from acid or alkali atmosphere.
2. Cleaned wires should be preserved in dry vessels.